Fortu Tech is an ISO Certified Corporation located in China and specializes in manufacturing C103 Niobium-Hafnium Alloy Rod & Bar.We have more than 20 years of production experience. Our products are Conflict Free material.
| Common specifications | ||||||||
| Diameter inch | 0.15 | 0.2 | 0.25 | 0.3 | 0.35 | 0.4 | 0.45 | 0.5 |
| Diameter mm | 3.81 | 5.08 | 6.35 | 7.62 | 8.89 | 10.16 | 11.43 | 12.7 |
Fortu Tech can customize the Nb10Hf alloys Rod according to your demand. Welcome to contact us if you have any questions or requirements.
C103 Niobium-Hafnium Alloy Bar of us meets the standard ASTM B655 R04295.
The bases of niobium 10 hafnium alloy Rod R04295 are niobium and hafnium alloys. Nb-C103 alloys Bar also contains some other elements, such as titanium, zirconium, vanadium etc.Nb C-103 alloys Rod's melting Point are 2350 ± 50ºC( 4260 ± 90ºF).Nb C-103 alloys Bar's density is 0.320 lbs./in.3 (8.85 gm./cm.3).
To ensure good mechanical and physical properties of Niobium Hafnium C103 alloys rod, the details of each production link need to be strictly checked.
Nb-C103 alloys machining to Nb-C103 alloys rod is feasible.
| ASTM B655 Chemical Requirements Niobium-Hafnium Alloy Rod&Bar R04295 | |||||||||
| Element % | Hf | Ti | C | O | N | H | Zr | W | Ta |
| Content Maximum % | 9-11 | 0.7-1.3 | 0.015 | 0.025 | 0.01 | 0.0015 | 0.7 | 0.5 | 0.5 |
If you have inquiry or want to discuss your design with us, please write email to us.
We will reply your email within 24 hours.
| Mechanical Properties of Nb C103 alloys Rod&Bar ASTM B655 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 56 000 min, psi | 40 000 min, psi | 20% |
| Room temperature: | 385 min, MPa | 275 min, MPa | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.050 in. [1.3 mm] and thinner in thickness
| Mechanical Properties of Nb C103 alloys Rod ASTM B655 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 54 000 min, psi | 38 000 min, psi | 20% |
| Room temperature: | 370 min, MPa | 260 min, MPa | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.051 in. [1.3 mm] and greater in thickness
Nb C103 Rod ASTM B655 is a high performance niobium alloy. Niobium C-103 Alloys Rod can be machined into parts of various shapes. Niobium Hafnium C103 alloys Rod can also be made into Nb10Hf Powder which is required by 3D printing industry. The powder can be printed into parts for rocket, jet and satellite propulsion. The diameter of the Columbium Nb-C103 bar can be selected according to the different using environment.
In addition to Niobium C-103 alloys Rod & Bar, we also produce Niobium C-103 alloys Ingot, Niobium C-103 alloys Sheet & Plate, Niobium C-103 alloys Wire, Niobium C-103 alloys Disc, Niobium C-103 alloys machined parts, Niobium C103 Alloy Spherical Powder. They meet Standard R04295, ASTM B 652, ASTM B 655, ASTM B 654, AMS 7852, AMS 7857.