Fortu Tech is an ISO Certified Corporation located in China and specializes in manufacturing C103 Niobium-Hafnium Alloy wire. We have more than 20 years of production experience. Our products are Conflict Free material.
| Common specifications | ||||||||
| Diameter inch | 0.01 | 0.02 | 0.03 | 0.04 | 0.05 | 0.08 | 0.1 | 0.125 |
| Diameter mm | 0.254 | 0.508 | 0.762 | 1.016 | 1.27 | 2.032 | 2.54 | 2.54 |
Fortu Tech can customize the Nb10Hf alloys wire according to your demand. Welcome to contact us if you have any questions or requirements.
C103 Niobium-Hafnium Alloy wire of us meets the standard ASTM B655 R04295.
The main components of niobium 10 hafnium alloy wire R04295 include niobium and hafnium alloys. Niobium C-103 alloys wire also contains a number of other trace elements, such as titanium, zirconium, vanadium and so on.Because these elements work together, Niobium C-103 wire has excellent corrosion resistance and high temperature properties.
The heat treatment process of columbium-hafnium alloy wire is important.
The elements can be evenly distributed after the process. It also ensure that the mechanical and physical properties of Nb C103 alloys wire are in the best condition.
Nb C103 alloys machining to Nb C103 alloys wire is feasible.
| ASTM B655 Chemical Requirements Niobium-Hafnium Alloy Wire R04295 | |||||||||
| Element % | Hf | Ti | C | O | N | H | Zr | W | Ta |
| Content Maximum % | 9-11 | 0.7-1.3 | 0.015 | 0.025 | 0.01 | 0.0015 | 0.7 | 0.5 | 0.5 |
If you have inquiry or want to discuss your design with us, please write email to us.
We will reply your email within 24 hours.
| Mechanical Properties of Nb C103 alloys wire ASTM B655 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 56 000 min, psi | 40 000 min, psi | 20% |
| Room temperature: | 385 min, MPa | 275 min, MPa | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.050 in. [1.27 mm] and smaller in diameter
| Mechanical Properties of Nb C103 alloys wire ASTM B655 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 54 000 min, psi | 38 000 min, psi | 20% |
| Room temperature: | 370 min, MPa | 260 min, MPa | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F [1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.051 in. [1.20 mm] and larger in diameter
Nb C103 wire ASTM B655 is a high performance niobium alloy.Niobium Hafnium C103 alloys wire is ideal for rocket, jet and satellite propulsion applications. Niobium C-103 wire can be made into Nb-C103 powder and become a 3D printing material. Nb10Hf wire has been widely used in the 3D printing industry. Niobium Hafnium alloys wire are used for the production of aerospace, plane components.Fortu Tech can customize the Nb10Hf alloys wire according to your demand. Welcome to contact us if you have any questions or requirements.
In addition to Niobium C-103 alloys wire, we also produce Niobium C-103 alloys Ingot, Niobium C-103 alloys Sheet & Plate, Niobium C-103 alloys Rod & Bar, Niobium C-103 alloys Foil, Niobium C-103 alloys Disc, Niobium C-103 alloys machined parts, Niobium C103 Alloy Spherical Powder. They meet Standard R04295, ASTM B 652, ASTM B 655, ASTM B 654, AMS 7852, AMS 7857.