Fortu Tech is an ISO Certified Corporation located in China and specializes in manufacturing C103 Niobium-Hafnium Alloy Sheet & Plate. We have more than 20 years of production experience. Our products are Conflict Free material.
| Common specifications | ||||||||
| Thickness inch | 0.15 | 0.2 | 0.25 | 0.3 | 0.35 | 0.4 | 0.45 | 0.5 |
| Thickness mm | 3.81 | 5.08 | 6.35 | 7.62 | 8.89 | 10.16 | 11.43 | 12.7 |
Fortu Tech can customize the Nb10Hf alloys Sheet according to your demand. Welcome to contact us if you have any questions or requirements.
C103 Niobium-Hafnium Alloy Plate of us meets the standard ASTM B654 R04295.
Melting Point of of Niobium C-103 alloys Sheet and Nb C-103 alloys Plate are 2350 ± 50ºC (4260 ± 90ºF). Density of Nb C-103 alloys Sheet and Nb C-103 alloys Plate is 8.85 gm./cm.3.
Nb-C103 alloys Sheet can support high stress levels at high temperatures.
The tensile strength of Nb-C103 alloys Plate at room temperature is greater than 370MPa. The yield strength of Nb-C103 alloys Sheet is above than 260MPa.The elongation of Niobium C-103 Alloys Sheet is greater than 20%.Nb-C103 alloys machining to Nb-C103 alloys plate is feasible.
| ASTM B654 Chemical Requirements Niobium-Hafnium Alloy Sheet&Plate R04295 | |||||||||
| Element % | Hf | Ti | C | O | N | H | Zr | W | Ta |
| Content Maximum % | 9-11 | 0.7-1.3 | 0.015 | 0.025 | 0.01 | 0.0015 | 0.7 | 0.5 | 0.5 |
If you have inquiry or want to discuss your design with us, please write email to us.
We will reply your email within 24 hours.
| Mechanical Properties of Nb C103 alloys Sheet ASTM B654 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 56 000 min, psi | 40 000 min, psi | 20% |
| Room temperature: | 385 min, MPa | 275 min, MPa | 20% |
| 2000+/- 25°F[1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F[1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.050 in. [1.3 mm] and thinner in thickness
| Mechanical Properties of Nb C103 alloys Sheet ASTM B654 | |||
| Ultimate Tensile Strength | Yield Strength | Elongation | |
| Room temperature: | 54 000 min, psi | 38 000 min, psi | 20% |
| Room temperature: | 370 min, MPa | 260 min, MPa | 20% |
| 2000+/- 25°F[1100 +/- 15°C]: | 21 000 min, psi | 16 000 min, psi | 20% |
| 2000+/- 25°F[1100 +/- 15°C]: | 145 min, MPa | 110 min, MPa | 20% |
Size: 0.051 in. [1.3 mm] and greater in thickness
Because Niobium Hafnium alloys Sheet not only is light weight and particularly owns good processing performance. Nb10Hf alloys Sheet is used in large quantities to produce lightweight propulsion systems and rocket engine thrust chambers. NbHf10Ti1Zr0.7 alloys Sheet is also a common material for space equipment. Turbopump and high-temperature jet engine parts are important parts in the industrial and aerospace industries. Their preferred material is Nb-Hf-Ti alloys.
In addition to Niobium C-103 alloys Sheet & Plate, we also produce Niobium C-103 alloys Ingot, Niobium C-103 alloys Foil, Niobium C-103 alloys Rod & Bar, Niobium C-103 alloys Wire, Niobium C-103 alloys Disc, Niobium C-103 alloys machined parts, Niobium C103 Alloy Spherical Powder.They meet Standard R04295, ASTM B 652, ASTM B 655, ASTM B 654, AMS 7852, AMS 7857.